Abstract
The energetic chemical reaction between Zn(NO3 )2 and Li is used to create a solid-state interface between Li metal and Li6.4 La3 Zr1.4 Ta0.6 O12 (LLZTO) electrolyte. This interlayer, composed of Zn, ZnLix alloy, Li3 N, Li2 O, and other species, possesses strong affinities with both Li metal and LLZTO and affords highly efficient conductive pathways for Li+ transport through the interface. The unique structure and properties of the interlayer lead to Li metal anodes with longer cycle life, higher efficiency, and better safety compared to the current best Li metal electrodes operating in liquid electrolytes while retaining comparable capacity, rate, and overpotential. All-solid-state Li||Li cells can operate at very demanding current-capacity conditions of 4 mA cm-2 -8 mAh cm-2 . Thousands of hours of continuous cycling are achieved at Coulombic efficiency >99.5 % without dendrite formation or side reactions with the electrolyte.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.