Abstract
Compared with some cobalt-rich cathodes which have been proven to yield high performance in SOFCs, interest in cobalt-free cathodes has increased due to their reduced thermal expansion coefficients (TECs), high structural stability, and CO2 tolerance. In this report, a new robust Co-free complex perovskite oxide PrLa0.4Ba0.6Fe0.8Zn0.2O5+δ (PLBFZ) has been synthesized and evaluated. The TEC is 14.4 × 10−6 K−1. With the introduction of Sm0.2Ce0.8O2 (SDC), the composite cathode PLBFZ-SDC with a mass ratio of 7:3 (PLBFZ-SDC 73) exhibited the best electrocatalytic activity for oxygen reduction under OCV conditions, with polarization values of 0.044, 0.079, 0.124, 0.251, 0.572, and 1.297 Ω cm−2 at 800, 750, 700, 650, 600, and 550 °C, respectively. The power densities of the cell were 1309, 1079, 788 and 586 mW cm−2 at 750, 700, 650, and 600 °C, respectively. Moreover, it appears to have good stability in air containing 1% CO2 (volume ratio) for 150 h based on Raman and polarization resistance (Rp) analysis. These results suggest that PLBFZ and its SDC composite are promising cathodes for IT-SOFCs.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.