Abstract
In fiber-reinforced polymer (FRP) composite laminate structures operating under fluctuating stresses, interface delamination is seen as one of the significant damage mechanisms. The constant degradation of their relatively low interlaminar strength and stiffness are the primary reasons for delamination. This study develops an interlaminar fatigue damage model to quantify the mechanics of the damage process and address the reliability of composite structures. The model considers the failure process in two stages: (1) damage due to degradation of interlaminar elastic properties, and (2) damage due to dissipation of fracture energy through the damage evolution process. The model is examined for a case study of mode I fatigue loading of a carbon-fiber-reinforced polymer (CFRP) composite laminate. The results show that the interlaminar normal stress is confined to the crack front region, with tensile stress peaks at 70% of the interlaminar strength. Furthermore, a stable interface crack growth is predicted initially, followed by a sudden crack "jump" at 14,000 cycles. The simulation results are compared with the experimental data, with very good agreement, showing a successful validation of the fatigue model.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.