Abstract
Strontium doped Cerium oxide (Ce1-0.25Sr0.25O2 and Ce1-0.5Sr0.5O2) nanocrystals were synthesized by combustion technique. The synthesized (Ce1-xSrxO2, x = 0.25, 0.5) nanocrystals were annealed at 500° C for 2hr. The phase formation, surface morphology and elemental composition analysis have been studied using XRD, HRSEM and EDXS. XRD and HRSEM measurements revealed that the synthesized nanocrystals were in single phase with face-centered cubic (fcc) structure and that the nano-grains had different sizes. Chemical composition was confirmed using EDXS. The UV-Vis spectroscopic studies revealed that as the Sr doping level increases, the band gap width increases from Eg = 2.9 eV to 2.95 eV. At the same time, the wavelength of maximum absorbance shifts from λabs = 285 to 300 nm. Further, PL studies were performed with excitation wavelength λ = 350 nm and two main emission peaks were observed at 415 and 437 nm respectively. TGA, DTA and DSC measurements were carried out to check the weight loss and the occurrence of endothermic/exothermic reactions
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.