Abstract
All-inorganic perovskite quantum dots (QDs), a promising semiconductor material, is suitable for new generation optoelectronic application. While there are many kinds of coating procedures for producing perovskite QDs peorovskite film, those methods require post-treatments and an additional dispersion support agent while still retaining pinholes and cracks. In this work, we report a facile method to produce CsPbBr3 film on a pre-patterned Pt electrode using a centrifuge coating method for photodetector (PD) application. Compact and crack-free films with ~500 nm thick from various particle sizes of 8 nm, 12 nm, and >30 nm were achieved with a suitable ratio of toluene/ethyl acetate solvent for visible light photodetector application. The optimized device has an on/off ratio of 103, detectivity of 3 × 1012 Jones, and responsivity of 6 A/W. In comparison, the on/off ratio of the device fabricated by the centrifuge coating method was 102 times higher than by the drop-coating method. The PD performance exhibited considerable moisture stability at mild high ambient temperature with no encapsulation for more than two weeks. The results suggest that this is a potential method for fabricating all inorganic perovskite nano-semiconductor films for further optoelectronic application in photodetectors, LEDs, and solar cells.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.