Abstract
A high-efficiency flame retardant composed of phosphaphenanthrene, benzothiazole and imidazole groups (PBI) was synthesized and served as flame retardant co-curing agent to reduce the fire hazard of epoxy resin (EP). The chemical structure of PBI was characterized by Fourier transform infrared spectroscopy (FTIR), high-resolution mass spectroscopy (HR-MS), 1H and 31P nuclear magnetic resonance (NMR). The curing behavior, thermal stability and flame retardant properties of the prepared EP systems were investigated. The curing behavior study disclosed that PBI accelerated the crosslinking reaction of EP and was chemically bonded with EP matrix to obtain intrinsic flame retardant thermoset. The resulting EP thermosets showed only slight decrease in glass transition temperature (Tg). The thermogravimetric analysis (TGA) results indicated both the catalytic decomposition and catalytic charring effects of PBI demonstrated by decreased thermal stability and enhanced charring capability of EP/DDS/PBI thermosets. The combustion test results showed remarkable improvement in the flame retardant properties of EP/DDS/PBI thermosets. When the phosphorus content was only 0.75 wt%, EP/DDS/PBI-0.75 thermoset achieved a limiting oxygen index (LOI) value of 34.6% and passed UL94 V-0 rating. Moreover, the peak of heat release rate (pk-HRR), average of heat release rate (av-HRR) and total heat release (THR) values were decreased by 48.7%, 31.1% and 28.3%, respectively, in comparison with those of the EP/DDS thermoset. The flame retardant effect of PBI on EP was attributed to the catalytic charring effect to form protective char layer in condensed phase and release of free radicals with quenching effect and nonflammable gases with diluting effect in gaseous phase.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.