A comprehensive characterization of 3D printable poly ether ketone ketone

Abstract

The current work focuses on the comprehensive characterization of a 3D printable biomaterial, polyether ketone ketone (PEKK). The PEKK granules are first characterized and then utilized for extrusion of the PEKK filaments. The extruded PEKK filaments are characterized for crystallinity, quality, and printability, wherein they exhibit amorphous nature, good quality, and appropriate printability. Utilizing the filaments, the samples are printed with the appropriate printing parameters, which are further characterized for layer adhesion, voids, and crystallinity, wherein they showed seamless layer adhesion, improper beads consolidation, and the amorphous nature. The as printed samples are further annealed at different temperatures (200 and 250 °C). The scanning electron microscopy (SEM) of the annealed samples (A-200 and A-250) revealed better void consolidation, while the X-ray diffraction (XRD) revealed better crystallinity compared to the un-annealed sample. The printed samples are also investigated for dynamic mechanical analysis (DMA), shape memory, and tensile properties. The storage moduli of the annealed samples are observed to be better than the un-annealed sample. The annealed samples exhibited better shape memory properties: shape fixity and shape recovery ratio of A-200 and A-250 samples, 90.28 and 90.75%, and 99.16 and 94.73%, respectively, compared to the un-annealed samples. The highest shape fixity ratio and the shape recovery ratio are noted for A-250 (90.75%) and A-200 (∼ 100%). The A-200 and A-250 samples showed enhanced tensile modulus and strength, 4.16 and 49.67%, and 36.61 and 35.06%, respectively compared to the un-annealed sample. The highest modulus is noted for A-250, while the strength is comparable (36.61 and 35.06%) for A-200 and A-250.