Abstract
In this study, two Mg based hydrogen storage composite powders, Mg–Y2O3 and Mg–Y, were prepared through arc plasma method followed by in situ passivation. The composition, phase component, and hydrogen storage properties of the two powders were analyzed by using ICP, XRD, PCT and DTA techniques. ICP analyses revealed a reduction in Y content of both powders when compared to their initial composition, especially for the Mg–Y powder (from 25wt% down to 0.58wt%). XRD results showed the presence of Y2O3 both in the Mg–Y2O3 and the Mg–Y powders. PCT analyses showed that the hydrogen storage capacity of the Mg–Y2O3 powder is higher than that of the Mg–Y powder. Based on van’t Hoff equation, the hydrogenation enthalpies of the Mg–Y2O3 and Mg–Y powders are determined to be −75.4 and −71.8kJ/molH2, respectively. DTA measurements showed that the onset dehydriding temperature of the hydrogenated Mg–Y2O3 powder is lower than that of the hydrogenated Mg–Y powder. The above results indicated that Y2O3 has a good catalytic effect on the hydrogen sorption in Mg and the effect can be better achieved in the arc evaporated Mg–Y2O3 composite powder.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.