Abstract
Two different processing routes are used to investigate the microstructure and strength of commercial purity (CP) titanium of grade 4 processed by equal‐channel angular pressing (ECAP). In the combined temperature (CT) route, the specimens are pressed at 723 K in the first pass and at 373 K in the second pass, but in the warm temperature (WT) route, the specimens are pressed through two passes at 723 K. Both routes lead to an inhomogeneous microstructure with an average grain size of ≈1.5 and ≈1.7 μm after the CT and WT routes, respectively. Both routes give improved strengthening and higher hardness, but the CT route with a lower temperature step gives the highest ultimate tensile strength of ≈790 MPa. The inclusion of a lower temperature processing step may be important for optimizing the strength of CP Ti for the use in medical implants.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.