Experiments were conducted to evaluate the microstructures and mechanical properties of a Cu–0.1 % Zr alloy processed using two different techniques of severe plastic deformation: equal-channel angular pressing (ECAP) and high-pressure torsion (HPT). The samples were processed at room temperature through ECAP for eight passes or through HPT for 10 turns. The results show HPT is more effective both in refining the grains and in producing a large fraction of grain boundaries having high angles of misorientation. Both procedures produce reasonably homogeneous hardness distributions but the average hardness values were higher after HPT. In tensile testing at 673 K, the highest strength and ductility was achieved after processing by HPT. This is attributed to the grain stability and high fraction of high-angle grain boundaries produced in HPT.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.