Abstract
We deal here with Sb and Bi doping effects of the n-type half-Heusler (HH) Ti0.3Zr0.35Hf0.35NiSn alloy on the measured thermoelectric properties. To date, the thermoelectric effects upon Bi doping on the Sn site of HH alloys have rarely been reported, while Sb has been widely used as a donor dopant. A comparison between the measured transport properties following arc melting and spark plasma sintering of both Bi- and Sb-doped samples indicates a much stronger doping effect upon Sb doping, an effect which was explained thermodynamically. Due to similar lattice thermal conductivity values obtained for the various doped samples, synthesized in a similar experimental route, no practical variations in the thermoelectric figure of merit values were observed between the various investigated samples, an effect which was attributed to compensation between the power factor and electrical thermal conductivity values regardless of the various investigated dopants and doping levels.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.