Abstract
Conventional and nanostructured WC-12wt.% Co powders were HVOF sprayed on Al7075-T6. The nanocoatings presented slightly less microporosity, higher microhardness, higher fracture toughness but higher decarburization, than the conventional ones. The nanocoatings exhibited greater resistance to general corrosion and localized corrosion in 3.5% NaCl than their conventional counterparts. Other than an occasional removal of WC nanoparticles, corrosion modes appeared similar for both types of coatings, characterized by selective dissolution of Co, formation of protective surface films and crevice corrosion along interlayer boundaries. Both types of coatings exhibited high dry sliding wear resistance. Nevertheless, the wear performance of the nanocoatings was even superior than that of their conventional counterparts. Main wear modes included plastic deformation of binder, oxidative wear leading to the formation of lubricating oxides and adhesive wear leading to the formation of alumina-rich surface depositions (from the Al2O3 counter balls). Coating of Al7075 with nano WC–12Co was proved effective in terms of microstructural features, corrosion and wear behaviour.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.