Abstract
In this study, the corrosion behavior of Ni47Ti49Co4 shape memory alloy (SMA) was investigated in simulated saliva solution with the binary alloy Ni51Ti49 as a reference. The surface morphology and the chemical composition of the oxide films were characterized by scanning electron microscopy and X-ray photoelectron spectroscopy before and after immersion in the test solutions, respectively. The results showed that the ternary alloy was less affected by the test solution, owning to the formation of passive layer composed mainly of the oxides of titanium and cobalt in several oxidation states. Cyclic voltammetry, electrochemical impedance spectroscopy and potentiodynamic polarization measurements affirmed that the passive oxide film significantly improved the corrosion resistance of Ni47Ti49Co4 SMAs as demonstrated by the smaller corrosion current density, larger resistance and smaller capacitance. Consequently, alloying with cobalt, which has paramount importance in enhancing the passive layer, expands the use of Ni47Ti49Co4 SMAs in dental work as new nitinol alloys with high corrosion resistances.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.