Abstract
A comprehensive study on Sn macrosegregation behavior in ternary Al-Sn-Cu alloys was carried out by comparative analysis between gravity casting and squeeze casting samples. The microstructure and Sn distribution of the castings were characterized by metallography, scanning electron microscopy (SEM), energy-dispersive X-ray (EDX) spectroscopy, and a direct reading spectrometer. Results show that there are obvious differences in Sn morphology between gravity casting and squeeze casting alloys. Under squeeze casting condition, the grain size of the casting is smaller and the distribution of β(Sn) is uniform. This effectively reduces the segregation of triangular grain boundary as well as the segregation of Sn. The segregation types of Sn in gravity casting and squeeze casting samples are obviously different. The upper surfaces of gravity casting samples show severe negative segregation, while all the lower surfaces have positive segregation. Compared with gravity casting, squeeze casting solidifies under isostatic pressure. Due to the direct contact between the upper surface of the casting and the mold, the casting solidifies faster under higher undercooling degree and pressure. Consequently, the uniform distribution of Sn reduces the segregation phenomenon on the surface of the casting.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.