Abstract
Cellulose nanocrystals (CNCs) and cellulose nanofibres (CNFs) were successfully extracted from cellulose obtained from maize stalk residues. A variety of techniques, such as Fourier transform infrared (FTIR) spectroscopy, scanning electron microscopy (SEM), X-ray diffraction (XRD) and thermogravimetric analysis (TGA) were used for characterization and the experimental results showed that lignin and hemicellulose were removed to a greater extent by following the chemical methods. Atomic force microscopy (AFM) results confirmed that the diameters of CNCs and CNFs were ranging from 3 to 7 nm and 4 to 10nm, respectively, with their lengths in micro scale. CNCs suspension showed a flow of birefringence, however, the same was not observed in the case of suspension containing CNFs. XRD analysis confirmed that CNCs had high crystallinity index in comparison to cellulose and CNFs. Nanopapers were prepared from CNCs and CNFs by solvent evaporation method. Micropapers were also prepared from cellulose pulp by the same technique. Nanopapers made from CNFs showed less transparency as compared to nanopapers produced from CNCs whereas high transparency as compared to micropaper. Nanopapers produced from CNFs provided superior mechanical properties as compared to both micropaper and nanopapers produced from CNCs. Also, nanopapers produced from CNFs were thermally more stable as compared to nanopapers produced from CNCs but thermally less stable as compared to micropapers.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.