Abstract
Corrosion behavior of TIG and laser welded Ti–5Al–2.5Sn alloy was compared using different electrochemical techniques. Bead on plate (BoP) configuration was used for welding of 1.6mm thick Ti–5Al–2.5Sn plates which led to the formation of complete α′ martensitic structure in laser welds and acicular α along with α′ martensite within coarse prior β grains was observed in TIG welds. Potentiodynamic and cyclic polarization were carried out in 5, 7 and 9M HNO3 to study the effect of concentration on the galvanic corrosion of laser and TIG welded Ti–5Al–2.5Sn. The oxide layer developed after 192h of immersion in fuming HNO3 was studied using electrochemical impedance spectroscopy (EIS) and SEM. All the samples showed good passivity but different oxidation behavior was observed mainly because of the surface modification after the welding operation.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.