Abstract
Creep rupture behaviour of modified type 316L(N) stainless steel base metal and weldments prepared with 16-8-2 filler wire has been investigated in air and flowing sodium environments at 823 K. No adverse environmental effects have been noticed due to sodium on the creep rupture behaviour of these weldments for tests up to 10 000 h. Rupture lives of the weldment were higher in the sodium environment than those in air. Rupture lives of the weldments were found to be lower than those of the base metal by a factor of two to five in both air and sodium environments. Minimum creep rates were essentially the same for the weldment as well as for the base metal in both the environments, whereas rupture strain was usually lower for the weldment than that of the base metal. The reduction in area of the weldment specimens increased with increase in stress. Failures in the specimens of weldmens were in the weld metal region. Microstructural studies carried out on failed weldment specimens after the creep rupture tests revealed extensive cavitation in the weld metal region in air tested specimens predominantly at the austerite/δ-ferrite interphase. However, no cavitation was observed in specimens tested in sodium.
Published Version
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callMore From: International Journal of Pressure Vessels and Piping
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.