Abstract
AbstractBa6Ta2O11 with an oxygen—deficient perovskite—related structure, was prepared through solid state reaction of BaCO3 and Ta2O5 powders. The electrical conductivity of sintered Ba6Ta2O11 pellets was measured by a.c. impedance spectroscopy inthe temperature range between 200 and 800ºC. The conductivity at 800ºC was3.7x10-3 Ω-1 cm-1; the activation energy for bulk conduction was 0.93 eV at temperatures between 500 and 800ºC and 1.22 eV below 500ºC. The bulk conductivity was independent of atmosphere, while the grain boundary conductivity, with an activation energy of 1.08 eV, decreased as oxygen partial pressure increased. The oxygen ion transport number obtained from concentration cell measurements was 0.5 to 0.65 at temperatures from 450 to 820ºC.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.