Abstract
High-voltage Schottky barrier diodes with low reverse leakage current were processed on hot-wall chemical vapor deposition grown 4H-SiC films. A metal overlap onto the oxide layer was employed to reduce electric field crowding at the contact periphery. By utilizing a 42–47 μm thick, high-quality epitaxial layers with doping in the range of 7×1014–2×1015 cm−3, a record blocking voltage of above 3 kV was achieved. The large diodes with 1.0 mm diameter showed breakdown at 2.1 kV. The reverse leakage current density at 1.0 kV was measured to be 7.0×10−7 A cm−2. Specific on-resistance of the diode with breakdown voltage at 3 kV was 34 mΩ cm2.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.