Abstract
Abstract The 57Fe enriched almost single-phase perovskites Pb(Fe0.5Nb0.5)O3 (PFN) and Ba(Fe0.5Nb0.5)O3 (BFN), prepared by a ceramic method (solid-state synthesis), were studied by Mossbauer spectroscopy, nuclear magnetic resonance (NMR), conventional and synchrotron X-ray powder diffraction (XRD). The temperature dependences of hyperfine and structural parameters of PFN, BFN from 4.2 K to temperatures above ferroelectric ordering of PFN (TS ∼ 375 K), with attention to the values of magnetic and structural transitions, were obtained. The antiferromagnetic magnetic ordering transitions were found under the Neel temperatures TN ∼ 167(3) K and 32(2) K for PFN and BFN, respectively. The spin-glass transition was at TG ∼ 10(3) K and 20(5) K for PFN and BFN, respectively. In PFN sample a small change of structural parameters around TN and structural change from trigonal to cubic structure at T ∼ 400 K was observed by XRD. The temperature dependence of XRD shows stable cubic structure in the temperature range from 4.2 K to 530 K for BFN. From Mossbauer and NMR spectroscopies it is found that both structures have perturbed environments for Nb and Fe. However, in case of PFN the low values of transferred hyperfine fields disfavour random Fe/Nb arrangement and allow proposing a picture of Fe/Nb arrangement.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.