Abstract
The work reported herein focuses on the 3D relative arrangement of individual platinum nanocrystals with a size of about 5 nm, and on the structure of the superlattices, they spontaneously form. Electron tomography was systematically used in this study because it allows obtaining quantitative 3D information in real space. Performing tomography in the bright-field TEM mode allowed investigating the short and long-range orderings of the nanoparticles packed as self-organized supercrystals. Systematic fcc pilings were observed with a mean lattice parameter measured to be 19.5 nm, the nature of the arrangement being controlled by the truncated octahedral morphology of platinum nanocrystals and the associated steric effects. A numerical 3D quantitative analysis of the ordering characteristics of the superlattice with a nanometer resolution has been performed that, for the first time, showed a direct correlation between single entities' characteristics and their ordering in periodic arrays. It has been shown that the lattice parameter is different in two orthogonal directions of the fcc structure, which indicates the presence of a slightly compressed superlattice. Inside the superstructure, vacancies and axial defects were observed that would blur the occurrence of potential collective effects from the supercrystals.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.