Abstract
In this study, strontium substituted hydroxyapatite (Sr-HAP) was synthesized using collagen type I and citrate as bi-templates and the obtained nanoparticles with high similarity to natural bone minerals were made into composite scaffolds with interconnected porous structure using a three-dimensional (3D) printing technique. A calcium deficient structure of HAP phase was caused by doping Sr which was verified by Fourier transform infrared, x-ray diffractometer, scanning electron microscopy and transmission electron microscopy. The Sr/(Sr + Ca) molar ratio in Sr-HAP nanoparticles was 5.8% estimated by EDX. Furthermore, both 3D printed scaffolds made of Sr-HAP and HAP had uniform porous structure and porosity of about 60%. Cell culturing indicated that MC3T3-E1 cells could adhere on the surface of the scaffolds and the strontium substitution could enhance cell adhesion, proliferation and alkaline phosphatase activity. The printed composite scaffolds were used to repair critical-sized rabbit calvarial defects with a diameter of 15 mm. The results showed that the Sr-HAP scaffolds had better osteogenic capability and stimulated more new bone formation within 12 weeks. It was suggested that these printed Sr-HAP composite scaffolds possessed high potential as candidates in the application of bone augmentation and regeneration.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.