Abstract
ABSTRACT This paper investigates the use of architected cellular and solid designs of materials via additive manufacturing and in-situ CO2 circulation to augment the carbonation and mechanical properties of a calcium silicate-based cement (CSC) binder. A wollastonite-based binder was formulated for extrusion-based 3D-printing. Solid and cellular lamellar architectures were designed to probe the role of layered interfaces and higher surface area on the degree of carbonation (DOC), respectively. Two carbonation exposure scenarios, with and without in-situ carbonation were employed. The DOC, microstructural phases, and flexural strength were characterised using TGA, modified over-flow image analysis technique, and three-point-bending, respectively. By exploiting 3D-printing and harnessing the higher surface area of cellular architecture, the material obtained a significantly higher DOC (by 8.9-folds) and flexural strength (by 5.7-folds) compared to reference cast. In-situ carbonation of cellular architected materials can additionally improve early-stage deformation, DOC (by 12.9-folds) and flexural strength (by 16.5-folds), compared to cast.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.