3D printing calcium phosphate ceramics with high osteoinductivity through pore architecture optimization

Abstract

The osteoinductivity of 3D printed calcium phosphate (CaP) ceramics has a large gap compared with those prepared by conventional foaming methods, and improving the osteoinductivity of 3D printing CaP ceramics is crucial for successful application in bone regeneration. Pore architecture plays a critical role in osteoinductivity. In this study, CaP ceramics with a hexagonal close-packed (HCP) spherical pore structure were successfully fabricated using DLP printing technology. Additionally, octahedral (Octahedral), diamond (Diamond), and helical (Gyroid) structures were constructed with similar porosity and macropore diameter. CaP ceramics with the HCP structure exhibited higher compression strength (8.39 ± 1.82 MPa) and lower permeability (6.41 × 10−11 m2) compared to the Octahedral, Diamond, and Gyroid structures. In vitro cellular responses indicated that the macropore architecture strongly influenced the local growth rate of osteoblast-formed cell tissue; cells grew uniformly and formed circular rings in the HCP group. Furthermore, the HCP group promoted the expression of osteogenic genes and proteins more effectively than the other three groups. The outstanding osteoinductivity of the HCP group was confirmed in canine intramuscular implantation studies, where the new bone area reached up to 8.02 ± 1.94 % after a 10-week implantation. Additionally, the HCP group showed effective bone regeneration in repairing femoral condyle defects. Therefore, our findings suggest that 3D printed CaP bioceramics with an HCP structure promote osteoinductivity and can be considered as candidates for personalized precise treatment of bone defects in clinical applications. Statement of significance1. 3D printing BCP ceramics with high osteoinductivity were constructed through pore architecture optimization.2. BCP ceramics with HCP structure exhibited relatively higher mechanical strength and lower permeability than those with Octahedral, Diamond and Gyroid structures.3. BCP ceramics with HCP structure could promote the osteogenic differentiation of MC3T3-E1, and showed the superior in-vivo osteoinductivity and bone regeneration comparing with the other structures.