Abstract
The advent of various additive manufacturing technologies, such as 3D printing, has changed the structural design and preparation process of rocket fuels. In order to investigate the combustion properties of various common polymer materials that can be additively manufactured by fused deposition, the combustion tests of hybrid rocket fuels prepared by 3D printing were carried out. These materials include polylactic acid (PLA), wood-like polylactic acid (Wood), acrylonitrile-butadiene-styrene (ABS), acrylonitrile-styrene-acrylate (ASA), copolymers of nylon 6 and nylon 6,6 (CoPA), polycarbonate-polybutylene terephthalate (PC-PBT), flame retardant polycarbonate (PC-FR) and polyethylene terephthalateco-1,4-cylclohexylenedimethylene terephthalate (PETG). Thermogravimetric-differential scanning calorimetry (TG-DSC) analysis was carried out on these materials, the printing effect of the fuel grains was observed by three-dimensional X-ray microscopy (µCT) and the combustion performance of these fuels in gaseous oxygen flow (GOX) was recorded by high-speed photography at a constant pressure of 1 MPa. The results show that ASA and ABS exhibit good printing results. The regression rates of PC-PBT, PETG, ABS, ASA, CoPA and PLA are 0.792 mm/s, 0.592 mm/s, 0.536 mm/s and 0.477 mm/s, 0.368 mm/s, 0.339 mm/s (AtGOX=220kg/(m2·s)), respectively.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.