3D pore analysis of gasoline particulate filters using X-ray tomography: impact of coating and ash loading

Abstract

Since particulate emissions control technologies are dependent on filtration technologies, development of porous materials with optimized pore structures is crucial to improve filtration efficiency and pressure drop across filters. Despite increasing attention to 3D measurements of porous materials, there are few reports of pore structure investigations of diesel/gasoline particulate filters (D/GPFs) using 3D visualization techniques. In this work, GPF 3D pore structures were examined using X-ray tomography (XRT) to identify the impacts of catalyst coating or ash loading. Voxel resolution of 2.93 µm made it impossible to distinguish coating or ash materials from the cordierite substrate or to recognize smaller pores than the voxel resolution. However, pores up to 200 µm, which are responsible for the most pore volume, were successfully analyzed. Coating and ash loading resulted in lowering average pore diameter, total porosity, and open porosity, as the peak density of pore diameter at 60 µm decreased, while pores below 20 µm increased. Also, the visualized closed pores, which were homogeneously distributed throughout the bare filter, tended to get larger from inlet to outlet sides and more likely to be on the surface inlet due to coating and ash loading, indicating gas pathways originally existing in open pores were blocked due to coating and ash loading, leading to increased pressure drop. The ash impact was found to be more noticeable on mid and back positions than on front position. In addition, the investigation of areal porosity along the direction of gas flow suggested that while ash penetration could reach the outlet side as noted from increased closed pore population, most ash particles would be contained up to 150 µm. The 2D crosscut microscopic analysis that requires destructive procedures with the limited examination area could provide underestimation of ash penetration, whereas the 3D XRT analysis seems to provide more accurate information of pore structure changes due to ash loading at different locations.