Abstract
Phosphosilicate thin film and monolith co-doped with Er3+-Yb3+ were prepared by self-modified Sol-Gel. Spin coating was used to deposit the prepared samples. The calculated crystallite sizes were found to be 26 and 28 nm for (S22P0.5E0.5YM) sintered at 500 and 1000 °C, respectively. A thickness of 1.6 μm was obtained for (S22P0.5E0.5YM). Laser-based Raman microspectroscopy presents the homogenous distribution of the Er3+&Yb3+ ions. The Er3+&Yb3+ absorption coefficients were measured. The radiative properties for the metastable level 4I13/2 were determined using The Judd–Ofelt model. The electron relaxation time (τr) slightly increased with the Yb3+ ions concentration up to 19.41 ms. Photoluminescence increased with increasing the Yb3+ ions. Pumping the 4F transition 4I13/2 → 4I15/2 of Erbium ions with 650 nm laser emits at around 1500 nm. This study introduces promising results for the prepared samples to support the planar optical waveguide amplifier system that could be used in communication and laser applications. However its cost-effectiveness, on-site measurability is still an interesting matter challenge.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.