Abstract
2inch size Ce:Gd3Al2Ga3O12 (Ce:GAGG) single crystals were grown by the Czochralski (Cz) method using [100] oriented seed. The crystals were up to 120mm in length and 50mm in diameter were achieved and had no cracks. Luminescence and scintillation properties were measured. In order to determine light yield, the energy spectra were collected under 662keV γ-ray excitation (137Cs source) were detected by a with avalanche photodiode (APD) S8664-55(Hamamatsu).The light yield of CeGAGG sample was calibrated from 55Fe direct irradiation peak to APD. The light yield was around 46,000photon/MeV. Energy resolution was 4.9%@662keV for 5×5×1mm sample. The theoretical density of CeGAGG is 6.63g/cm3.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.