The effects of sintering additives of magnesium silicates, i.e. enstatite (MgSiO3), steatite (MgSiO3) and forsterite (Mg2SiO4), on the sintering behaviors and characteristics of the silicon nitride ceramics-based inert matrix fuels (IMFs) were experimentally investigated. Fabrication tests and characterizations of Si3N4-based IMFs with the sintering additives were carried out using cerium oxide (CeO2) to represent minor actinide oxides. Sintered bodies were characterized in terms of their densities and thermal conductivities. In addition, a solubility test with hot nitric acid was carried out for evaluation of applicability to the existing reprocessing technology. The densification of sintered bodies was enhanced by using additives of magnesium silicates at relatively low sintering temperature. In particular, the relative density of Si3N4-based IMFs with Mg2SiO4 was above 90% at 1723 K. The thermal conductivities of Si3N4-based IMFs varied according to sintering temperature, and for the IMFs sintered at 1923 K were above 34 W/m K. The solubility test results revealed that only grain boundary phases in Si3N4-based IMFs can be dissolved into hot nitric acid.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.