Abstract
The domain structures, dielectric properties, and phase transformation of (001)-oriented Pb(Mg 1/3 Nb2/3 )O₃-x%PbTiO₃ (PMN-x%PT) crystals for x=20, 30, 35, and 40 mole% have been investigated. PMN-20%PT consists of polar nano-domains (PND) which do not self-assemble into macro-domain plates. PMN-30%PT consists of PNDs which begin to self-assemble into colonies along preferred {110} planes. PMN-35PT consists of miniature polar domains on the nm scale. PMN-40%PT consists of {001} oriented lamella domains on the mm scale that have internal nano-scale heterogeneities. The dielectric properties of poled (001) PMN-x%PT single crystals have been measured for orientations both parallel and perpendicular to the [001] poling direction. The results of the temperature dependence of the dielectric constant and mesh scans for the 30%PT sample demonstrate that the initial monoclinic phase changes to single domain tetragonal phase and to cubic phase with increasing temperature.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.