As a shrinkage of Ti(N, C)-30wt%Ni mixed powder compacts during sintering was remarkably promoted not only in vacuum, but also in argon, hydrogen and nitrogen atmosphere without an abnormal expansion, we concluded that the abnormal expansion during sintering of TiN-TiC-Ni mixed powder compacts1) was caused by denitrification which took place during the formation of Ti(N, C) solid solution.Grain growth of sintered bodies was suppressed with an increase of nitrogen content of the nitrocarbide.In sintering of TiNx-TiCy-30wt%Ni mixed powder compacts, the expansion was arrested; the composition showing the maximum sintered density in the sintering condition at 1500°C for 1 hr. was TiN0.6-15wt%TiC-30wt%Ni.Use of TiCy powders also prevented the occurrence of the abnormal expansion during sintering.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callMore From: Journal of the Japan Society of Powder and Powder Metallurgy
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.