Abstract
Fe-doped skutterudite <TEX>$CoSb_3$</TEX> with a nominal composition of <TEX>$Fe_{x}Co_{4-x}Sb_{12}(0\;{\le}\;x\;{\le}\;2.5)$</TEX> has been synthesized by mechanical alloying (MA) of elemental powders, followed by hot pressing. Phase transformations during mechanical alloying and hot pressing were systematically investigated using XRD. Single phase skutterudite was successfully produced by vacuum hot pressing using as-milled powders without subsequent annealing. However, second phase in the form of marcasite structure <TEX>$FeSb_2$</TEX> was found to exist in case of <TEX>$x\;{\ge}\;2$</TEX>, suggesting the solubility limit of Fe with Co in this system. Thermoelectric properties as functions of temperature and Fe contents were evaluated for the hot pressed specimens. Fe substitution up to x=1.5 with Co in <TEX>$Fe_{x}Co_{4-x}Sb_{12}$</TEX> appeared to increase thermoelectric figure of merit (ZT) and the maximum ZT was found to be 0.78 at 525K in this study.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.