Abstract

Using the HSC 6.1 Chemistry (Outokumpu) software package in combination with simplex-lattice planning, we performed thermodynamic modeling of the equilibrium cerium content in a metal containing 0.06% C, 0.25 Si, 0.05% Al (in this expression and further on the text indicates mass%), under the slag of the CaO – SiO2 – Ce2O3 – 15% Al2O3 – 8% MgO system in a wide range of chemical composition at temperatures of 1550 °C and 1650 °C. For each temperature, adequate mathematical models have been obtained in the form of a reduced polynomial of degree III, describing the equilibrium content of cerium in the metal depending on the composition of the slag. The results of mathematical modeling are presented graphically in the form of diagrams of the composition – the equilibrium content of cerium. A marked effect of slag basicity on the distribution of cerium is noted. An increase in slag basicity from 2 to 5 at a temperature of 1550 °C leads to an increase in the equilibrium cerium content in the metal from 0.1 to 7 ppm, i.e. the increase in slag basicity favorably affects the development of cerium recovery process. An increase in metal temperature has a positive effect on cerium recovery. As the temperature rises to 1650 °C, the equilibrium cerium content in the metal increases on average from 0.3 to 10 ppm. In the diagrams of the chemical composition of slags containing 56-61% CaO, 12-14% SiO2 and 15% Al2O3 in the temperature range of 1550 and 1650 °C, we can expect a concentration of cerium in the metal at a level of 7-10 ppm at a content of 4% to 7% Ce2O3 in the original slag. The positive effect of the basicity of the formed slag in the studied range of chemical composition on the cerium reduction process is explained from the standpoint of the phase composition of the slag and the thermodynamics of cerium reduction reactions.

Talk to us

Join us for a 30 min session where you can share your feedback and ask us any queries you have

Schedule a call

Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.