Abstract : Self-piercing riveting (SPR) process is gaining popularity due to its many advantages. The SPR does not require a pre-drilled hole and has capability to join a wide range of similar or dissimilar materials and combinations of materials. This study investigated the fatigue strength of self-piercing rivet joint with aluminum alloy (Al-5052) and steel (SPCC) sheets. Static and fatigue tests on tensile-shear specimens were conducted. From the static strength aspect, the optimal punching force for the specimen with upper SPCC (U.S) sheet and lower aluminum alloy(L.A) sheets was 34 kN. During static test the specimens fractured in pull-out fracture mod e due to influence of plastic deformation of joining area. There was a relationship between applied load amplitude and number of cycles ; and for U.S-L.A and U.A-L.S specimens, respectively. U.A-L.S fatigue specimens failed due to fretting crack initiation around the rivet neck between upper and lower sheets.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.