오존산화 콩기름 변성 pMDI 접착제의 고온 및 중온 경화 접착력

Abstract

This study was to investigate the dry bond strengths of the plywoods manufactured with 3 hours ozonized soybean oil (SBO)/polymeric methylene diphenyl diisocyanate (pMDI) adhesive at mid and high curing temperature. In results of the dry bonding strengths of the 3 hrs-ozonized SBO mixed with pMDI at high curing temperature were respectively the strengths of weight ratio of 3hrs-ozonized SBO : pMDI, 1 : 0.5, 4.74 kgf/, 1 : 0.75, 7.14 kgf/ 1 : 1, 9.29 kgf/, 1 : 2, 16.53 kgf/, 1 : 3, 17.42 kgf/, and 1 : 4, 16.75 kgf/. Therefore, it was found that the equivalent ratio was formed approximately between 3 hrs-ozonized SBO : pMDI 1 : 2 and 1 : 3. The dry bonding strengths of the 3hrs-ozonized SBO mixed with pMDI at medium curing temperature were respectively the strengths of weight ratio of 3 hrs-ozonized SBO : pMDI, 1 : 0.5, 3.16 kgf/, 1 : 0.75, 6.13 kgf/ 1 : 1, 8.18 kgf/, 1 : 2, 11.82 kgf/. In this experiment the higher bonding strength at high curing temperature was shown approximately between 3 hrs-ozonized SBO : pMDI 1 : 2 and 1 : 3. If this wood adhesive is used at high curing temperature, it is possibile to bond the plywoods.