In order to reduce signal delay in ULSI, an intermetal material of low dielectric constant is required. Ordered mesoporous silica film is proper to intermetal dielectric due to its low dielectric constant and superior mechanical properties. The ordered mesoporous silica film prepared by TEOS (tetraethoxysilane) / MTES (methyltriethoxysilane) mixed silica precursor and Brij-76 surfactant was surfacemodified by HMDS (hexamethyldisilazane) treatment to reduce its dielectric constant. HMDS can substitute -Si(CH₃)₃ groups for - OH groups on the surface of silica wall. In order to modify interior silica wall, HMDS was treated by two different processes except the conventional spin coating. One process is that film is dipped and stirred in HMDS/n-hexane solution, and the other process is that film is exposed to evaporated HMDS. Through the investigation with different HMDS treatment, it was concluded that surface modification in evaporated HMDS was more effective to modify interior silica wall of nano-sized pores.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.