Abstract
The crystallization behavior and microstructural change of the glass-ceramics were analyzed as a function of concentration and etching time of the HF solution in order to enhance the degree of crystallinity induced by heterogeneous nucleation of glass of bottom ash containing 15 wt% Li₂O. The nucleation site seemed to be generated where the Si ion was eluted. The main crystal phases in the glass-ceramics fabricated in this study were β-spodumene and Li₂SiO₃. The specimens etched with HF of 0.5 vol% within 0~60 seconds showed increased crystalline peak intensities in XRD pattern with etching time compared to no-etched one. Also the crystal size and crystal occupancy in the glass matrix observed by SEM were increased with etching time. For the glass-ceramics etched with 1.0 and 2.0 vol% HF solution, the etching time over 10 s was not effective to increase the crystallinity. From this study, it was found that the glass-ceramics with the higher crystallinity could be obtained by HF-etching followed by heat treatment process, even though the nucleating agent or 2-stages thermal treatment process were not used.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.