Abstract
GaSb films were grown by molecular beam epitaxy using AlSb/As/Si transition layers on vicinal Si (001) substrates deflected 6 to the (111) plane. The influence of the GaSb films crystallographic orientation on their structural properties and surface morphology is investigated. It was found that GaSb(001 ̅)/Si films are characterized by better structural perfection, lower concentration of point defects and more planar and isotropic surface topography, compared with GaSb(001) films. Possible reason for the observed differences between GaSb films with different orientations is increased density of antiphase domains in GaSb(001) films. The morphological features of the grown films are caused by the terraces edges basically and by the anisotropy of the incorporation of Ga adatoms into the terraces edges, to a lesser extent.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.