Abstract
AbstractIt is shown that annealing 550°C of the Fe/Pt bilayer films fabricated by layer-by-layer deposition onto polycrystalline Al_2O_3 substrates in an atomic ratio of Fe: Pt = 71: 29 leads to the formation of the inplane rotational magnetic anisotropy with the easy axis that can be aligned by magnetic field in any direction in the film plane. The increase in the Pt content in the investigated film system to 50 at % leads to an increase in the anisotropy constant to 6.5 × 10^6 erg/cm^3, which exceeds the value in the Fe_71Pt_29 sample by a factor of 6. In addition to the rotational anisotropy, the Fe50Pt50 films are characterized by the perpendicular rotational magnetic anisotropy, which is higher than the film shape anisotropy. Therefore, the easy axis in these samples can be aligned by magnetic field in any spatial direction. According to the X-ray and magnetic measurement data, the synthesized samples have a polycrystalline structure consisting of two ordered phases: magnetically hard L1_0–FePt and magnetically soft L1_2–Fe_3Pt. This gives us grounds to suggest that the rotational magnetic anisotropy originates from the epitaxial intergrowth and exchange coupling of these two phases.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.