Abstract
Iron Aluminide Fe2Al5 has a rigid framework of both fully occupied Al and Fe sites and chains of partially occupied Al sites. On the other hand, Fe4Al13 possesses a large unit cell with 102 atoms. These complex and peculiar crystal structures bring a low lattice thermal conductivity. Here, we report the thermoelectric properties and discuss how the chain structure and large unit cell can lead to a low lattice thermal conductivity. The calculated room-temperature lattice thermal conductivity by using the Wiedemann-Franz law is approximately 1.5 W/mK and 0.8 W/mK for Fe2Al5 and Fe4Al13, respectively. From the comparison with other Fe-Al alloys, which have neither plural partially occupied sites nor a large unit cell, we found that (1) the heat capacity does not decrease at high temperature, i.e. Al atoms at partially occupied sites do not behave as liquid, (2) the speed of sound for Fe2Al5 and Fe4Al13 is almost identical among Fe-Al alloys, i.e. the average phonon group velocity of acoustic modes for Fe2Al5 and Fe4Al13 is not slower than that of Fe-Al alloys, (3) the electrical conductivities of Fe2Al5 and Fe4Al13 are lower than those of the other Fe-Al alloys. These results suggest that the low lattice thermal and electrical conductivities are brought by short relaxation times of both phonons and electrons due to chemical disorder such as the partially occupied sites. In particular, the unit cell of the Fe4Al13 includes 102 atoms, which beneficially reduce the lattice thermal conductivity. The maximum dimensionless figure of merit is approximately 0.02 for both Fe2Al5 and Fe4Al13 at 973 K.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
More From: Journal of the Japan Institute of Metals and Materials
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.