Abstract
Abstract For the steel structures those are used in harsh sea environments, corrosion fatigue is a challenging issue in connection with design life. In this research, in order to investigate the influence of cathodic overprotection on the corrosion fatigue crack propagation behavior, corrosion fatigue crack propagation test under the condition of -950mV vs SCE was conducted by using of high tensile TMCP steel plate and the relationships between da/dN-ΔK were obtained. At this test, when ΔK is low, the crack propagation rates were accelerated compared to those of seawater condition, however, when ΔK is high, the crack propagation rates were lower than those of seawater condition. As the cause for the acceleration and deceleration of corrosion fatigue crack propagation rates under the condition of cathodic overprotection, the role of hydrogen and calcareous deposits are discussed. Key Words : Fracture Mechanics, Corrosion Fatigue, Cathodic Overprotection, Synthetic Seawater 본 논문은 울산과학대학교 연구과제로 수행되었음.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callMore From: Journal of the Korea Academia-Industrial cooperation Society
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.