Studies are made on stress relief embrittlement of duplicated weld HAZ for 50 kgf/mm2 HTS. Degree of stress relief embrittlement expressed by Δ∇Ts is a function of weld thermal cycle cooling rate, and results showed that the highest notch toughness of stress-relieved weld HAZ was achieved in microstructure containing slight polygonal ferrite. That sort of microstructure can be obtained with thermal cycles cooling time of around 30 seconds from 800°C to 500°C for steels investigated, which shows the effectiveness for obtaining the safety of welded joints and the efficiency of welding fabrication by using comparatively high heat input of around Cf cooling time in SH-CCT diagram.Furthermore, grain boundary fracture was little found for both as duplicated and duplicated and stress-relieved HAZ, showing the significance of niobium and vanadium nitride and carbide coherent precipitation for stress relief embrittlement in weld HAZ, as it occurs transgranular cleavage fracture easily.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.