The structure and properties of ceramics based on zirconium dioxide stabilized yttrium oxide with the addition of high-modulus inclusions of carbon nanotubes were investigated. The composite materials were obtained by spark plasma sintering. The introduction of carbon nanotubes provides a slight decrease in the density and grain size of ceramics. Growth of volume fraction of carbon nanotubes leads to increase of mechanical properties of ceramic composites. The highest values of mechanical properties were obtained by the introduction of 5 vol.% of carbon nanotubes and were E = (246±8) GPa, H = (12.7±0.21) GPa, K 1 CI = (12.1±0.35) MPa∙m1/2, K 1 CN = (7.8±0.29) MPa∙m1/2. The increase of fracture toughness when carbon nanotubes are introduced into the ceramic matrix is caused by two dissipative mechanisms - phase transformation from tetragonal to monoclinic modification of ZrO2 and crack bridging. As the amount of introduced additive increases, the contribution of martensitic transformation in fracture resistance decreases, which is associated with a decrease in the grain size of the tetragonal zirconium dioxide phase and, accordingly, its transition to a stable state.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.