Abstract
Hard diamond-like-carbon (DLC) films were deposited on aluminum alloy (JIS A6063) substrate by RF plasma CVD using CH4 and H2 as reactant gas. CH4 concentration, deposition time, and RF power were varied to determine preferable deposition conditions that would not cause undesirable softening of the substrate during the deposition process. The thickness of DLC film was about 4μm under conditions of gas pressure: 27Pa, CH4: 30%, RF power: 300W, and deposition time: 3h.Friction and wear experiments were conducted using a reciprocating friction and wear test apparatus. DLC film deposited under the above conditions was slid against bearing steel (JIS SUJ 2) balls to investigate fundamental friction and wear properties from room temperature to 200°C. The results were compared with those for substrate without the deposited DLC film. With the DLC film, friction and wear in the aluminum alloy were greatly reduced up to 100°C. The above results suggest that DLC film should improve the tribological performance of aluminum alloys used for sliding parts.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.