Влияние твердофазной рекристаллизации с двойной имплантацией на плотность структурных дефектов в ультратонких слоях кремния на сапфире

Abstract

The main technological problem in the manufacture of electronics on silicon-on-sapphire (SOS) wafers is the high density of defects in the epitaxial silicon layer. The modern method of obtaining ultrathin SOS wafers using solid-phase epitaxial recrystallization (SPER) and pyrogenic thinning that significantly reduce the defect density in these layers. Nevertheless, the influence of the defect density in submicron SOS layers on the structural quality of ultrathin SOS layers remains unclear. In this work, ultrathin (100 nm) SOS wafers were obtained by SPER of submicron (300 nm) SOS wafers with different structural quality. The crystallinity of 300 nm layers before the recrystallization process and ultrathin layers was determined by XRD and TEM. It was found that the smallest values of the FWHM 0.19-0.20° were observed for the ultrathin SOS layers obtained on the basis of 300 nm SOS wafers with the best structural quality. It was shown that the structural perfect near-surface Si layer, which serves as a seed layer in SPER process, and the double implantation regime allow to reduce the linear defect density in the ultrathin SOS layers by ~ 1×104 cm-1.