In this study, we investigated the traits of the clad metals used in hot-rolled clad steel plates. We examined the sensitization and mechanical properties of STS 316 steel plate and carbon steel (A516) under the specific circumstances of post heat treatment and whether a weld was multilayered and thick or repeated because of repairs. The test conditions were as follows. The clad steel plates were butt-welded using FCAW/SAW, and the heat treatment was conducted at <TEX>$625^{\circ}C$</TEX>, for 80, 160, 320, 640, or 1280 min. The change in the corrosion resistance was evaluated in these specimens. In the case of the carbon steel (A516), as the heat treatment time increased, the annealing effect caused the tensile strength to decrease. The micro- hardness gradually increased and then decreased after 640 min. The elongation and contraction of the area increased gradually. An oxalic acid etch test and EPR test on STS316, a clad metal, showed a STEP structure and no sensitization. From the test results for the multi-layered and repair welds, it could be concluded that there is no effect on the corrosion resistance of clad metals. In summary, the purpose of this study was to suggest some considerations when developing on-site techniques and evaluate the sensitization of stainless steels.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callMore From: Journal of manufacturing engineering & technology
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.