Abstract
The diffusion hardening steel can be produced in any plant having a thermal equipment, besides, it is more economical than obtaining an alloy steel with similar properties. The influence of the parameters of the diffusion of chromium plating (the composition of the steel, powder mixture) on the structure and mechanical properties of structural and tool steels was investigated. Results of X-ray analysis showed that the diffusion zone in the samples consists of two layers. First layer is predominantly carbides Cr 7C 3, Cr 23C 6, Fe 3C. An intermediate layer composed of carbon-free solid solution of chromium in the iron. The maximum total thickness of the diffusion zone is observed in the steel 130Cr12V1 and 130Cr12Mo1 (~80 µm), minimum in carbon steels 45, U10 (~10-30 µm). The thickness of carbide layer is approximately the same 1-3 µm. Analyzing of data micro-hardness measurement across the thickness of the diffusion zone it must be noted that the diffusion layers of the samples of the tool steels have a high micro-hardness 6000-10000. The maximum HV=10200 was in steel 30Cr2W8V1. Chromium saturation of steel surface significantly increases its wear resistance. A much greater effect of increase of coefficient of relative wear resistance (3 fold increase) was observed in steels 30Cr2W8V1, 130Cr12V1 and 130Cr12Mo1. The mathematical models relating the micro-hardness, wear resistance, the thickness of the diffusion layer were obtained. In view of the analytical relationships ascertained that the wear resistance of hardened steels substantially depend on the thickness of the diffusion coating, the microhardness of the layer and the core of steel and alloy steels has increased more than two times. For hardening steel punching tool 30Cr2W8V1 can be recommended composition of the powder mixture: 50% FeCr + 48% Al 2O 3 + 2% NaF, and for steel 130Cr12V1 preferably used as activator NH 4F
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.