인-질소 화합물 조합에 의해 처리된 목재의 연소성

Abstract

This study was to investigate the characteristics of combustion toxic gases of pinus rigida specimens treated with chemical additives such as pyrophosphoric acid (PP)/ammonuium ion (), methylenepiperazinomethyl-bis-phosphonic acid (PIPEABP) and . Each pinus rigida plates was painted in three times with 15 wt% of each chemical additives in the aqueous solution. After drying these specimens at room temperature, the production of combustion gases and smoke was examined by the cone calorimeter (ISO 5660-1). As a result, the peak mass loss rate time (PMLR time) treated with chemicals was delayed upto 10.5~47.4% compared to that of using untreated specimen. In addition, the peak production of carbon monoxide () of 32.1~71.4% and total smoke release rate (TSRR) of 15.6~43.6% for test pieces treated with the chemical additive were higher than that of using the virgin plate. In particular, for the specimens treated with the chemical additive, the rate of smoke release (RSR) 29.4~41.5% was obtained higher than that of untreated plate except the specimen treated with . It can thus be concluded that the treatment using the chemical additive could partially increase the combustion-retardation properties of the species when compared to those of the virgin plate.