Abstract

Mixtures of Ti, Ni and TiB2, TiC or SiC powders were spark- and resistance-sintered to obtain TiB2, TiC or SiC dispersed TiNi pseudoelastic alloy. The alloys were annealed, solution treated and aged after the sintering. Nano-indentation tests, bending tests, and abrasion wear tests were carried out on these alloys. Nano-indentation tests showed that the TiNi alloy and ceramics-dispersed TiNi alloys exhibited larger displacement recovery than the reference materials such as steels and titanium alloy at the same indentation displacement. The solution treated and aged specimens exhibited larger displacement recovery than the annealed ones. Vickers hardness of the annealed alloys increased with increasing ceramics content, while relative density and bending strength decreased. TiB2 dispersed TiNi alloy has higher hardness than TiC dispersed TiNi alloy and larger bending strength than SiC added alloy. Abrasive wear resistance of TiB2 dispersed TiNi alloy was much larger than that of the steels and titanium alloys, which can be explained by the stress relaxation of pseudoelastic matrix surrounding ceramics particles. In addition, the TiNi alloys annealed after sintering exhibited better wear resistance than the solution treated and aged ones. The wear resistance of TiB2 dispersed TiNi alloy was larger than that of TiC dispersed TiNi alloy perhaps because of larger interfacial strength between TiB2 particles and TiNi matrix than that of TiC particles and TiNi matrix.

Talk to us

Join us for a 30 min session where you can share your feedback and ask us any queries you have

Schedule a call

Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.