Abstract
This study of rapid sinteing method within a few minutes is to investigate under nitrogen atmosphere. Specimens were composited 0.8mass%C-1.5mass%Cu-bal.Fe powders and used by the high frequency induction heating instrument. In this case, it was important to release an adsorbed gas in iron powder particle surface. The product of decarburized layer on specimen surface was a problem because of reduce of mechanical properties. As a result, it was possible to keep about 40μm at a minimum as the decarburized layer when the constant sintering condition (1523 K-30s, LT 1323 K-60s and heating rate 10 K/s). This method was finished to sinter only 3.5 minites, and the radial crushing strength (R.C.S) was obtained almost same value compared to conventional furnace method.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
More From: Journal of the Japan Society of Powder and Powder Metallurgy
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.